Size and Surface Chemistry Tuning of Silicon Carbide Nanoparticles

Chemical transformations on the surface of commercially available 3C-SiC nanoparticles were studied by means of FTIR, XPS, and temperature-programmed desorption mass spectrometry methods. Thermal oxidation of SiC NPs resulted in the formation of a hydroxylated SiO2 surface layer with C3Si–H and CHx groups over the SiO2/SiC interface. Controllable oxidation followed by oxide dissolution in HF or KOH solution allowed the SiC NPs size tuning from 17 to 9 nm. Oxide-free SiC surfaces, terminated by hydroxyls and C3Si–H groups, can be efficiently functionalized by alkenes under thermal or photochemical initiation. Treatment of SiC NPs by HF/HNO3 mixture produces a carbon-enriched surface layer with carboxylic acid groups susceptible to amide chemistry functionalization. The hydroxylated, carboxylated, and aminated SiC NPs form stable aqueous sols.

ID: 200018
Кількість показів: 58
дата змінення: 04.12.2017 14:14:55
Ким змінено (ім'я): (chem12) Анна Трохименко
Вид роботи:  Наукова публікація
Тип роботи:  Наукова стаття
Кількість сторінок:  11
Рік видання:  2017
Звітний рік:  2017
Видання:  Langmuir
Випуск, частина:  3
Номери сторінок:  1-11
Галузь науки:  Хімія
Автори,співробітники Університету:  Алексєєв Сергій Олександрович / Гринь Світлана Валеріївна / Коритко Дмитро Михайлович
Кількість недоданих авторів:  5
Кафедра / Відділ:  Кафедра супрамолекулярної хімії  / Аналітичної хімії / НДЛ Хімічного аналізу об'єктів навколишнього середовища та контролю виробництва
№ теми:   / 
Посилання на статтю (посилання на рецензію в журналі (для монографій):  http://pubs.acs.org/doi/abs/10.1021/acs.langmuir.7b02784?journalCode=langd5
Опубліковано за рішенням Вченої ради:  ні
Інститут/Факультет:  Хімічний факультет / Інститут високих технологій

Повернення до списку

Вгору