Using the method of continuous microindentation with different loading on the indenter, the
microhardness of compacted thermo-expanded graphite (TEG) samples of different dispersion was studied.
The analysis of the obtained results showed that, with an increase in the average cross-sectional area of
TEG particles from 40 to 120 microns, the microhardness of the samples under investigation also increases.
An analysis of the influence of the dispersion and morphology of the TEG particles on the distribution of
microhardness on the surface of the compacted samples of TEG was also carried out. The microhardness
indicatrix for the samples of the original TEG shows that when the radial displacement from the center of the
sample, the microhardness of the material decreases. So in the central part of the discoid sample the values
of microhardness lie in the range from 0,04 to 0,025 GPa. In the next concentric region, the microhardness
decreases by 30% and gains a value of (0.028 ... 0.014) GPA. When the dispersion of TEG particles
changes, the distribution of microhardness also changes. The microhardness indicatrix for a compacted Tg
sample with an average particle size of 180 μm shows that the microhardness value at the center of the
sample ranges from 0.065 to 0.15 GPa.As you approach the edge of the sample, the microhardness of the
material decreases from 0.15 to 0.054 GPa. The study of TEG with an average particle size of 50 μm showed
that the indentation in the center and in the middle region of the sample gives an isotropic distribution of
microhardness values. The microhardness values coincide in the central and middle regions of the sample
and correspond to ≈ 0.1 GPa. The proposed method of research and analysis of microhardness on the
surface of compacted specimens of TEG gives an opportunity not only to characterize the micromechanical
properties of the investigated material but also to optimize the technological regimes for obtaining samples.

ID: 241771
Кількість показів: 13
дата змінення: 24.12.2019 23:22:45
Ким змінено (ім'я): (mechmat15) Олена П'ятецька
Вид роботи:  Наукова публікація
Тип роботи:  Наукова стаття
Кількість сторінок:  4
Рік видання:  2019
Звітний рік:  2019
Видання:  Вісник Київського університету. Серія: фізико-математичні науки
Випуск, частина:  1
Номери сторінок:  173-176
Галузь науки:  Математика
Автори,співробітники Університету:  Андрущенко Володимир Олександрович / Мельниченко Микола Миколайович / Рево Сергій Лукич / Авраменко Тетяна Григорівна / Іваненко Катерина Олексіївна
Кафедра / Відділ:  Теоретичної та прикладної механіки
№ теми:  18БП038-01
Ключові слова:  Мікротвердість, компактований термічно розширений графіт
Опубліковано за рішенням Вченої ради:  ні
Інститут/Факультет:  Механіко-математичний факультет

Повернення до списку

Вгору